Abstract
The corrosion behavior of the pre-oxidized GH4169 alloy was studied after 20 h of exposure under a solid NaCl deposit film in a wet O2 environment at 600 °C by mass-gain measurements, X-ray diffraction, scanning electron microscopy, transmission electron microscopy methods. The results indicate that the pre-oxidized GH4169 alloy undergoes serious corrosion in the corrosive condition. The preformed Cr2O3 layer is gradually destroyed by deposit NaCl, and the inner Nb2O5 layer beneath the complete outer Cr2O3 layer also reacts with NaCl to form NaNbO3. The electrochemical test results testified the existence of electrochemical reactions during this corrosion process. The corrosion behavior of pre-oxidized GH4169 under a solid NaCl deposit film in a wet O2 environment at 600 °C has been discussed in detail.
Similar content being viewed by others
References
M. Cao, L. Liu, Z.F. Yu, L. Fan, L. Ying, F.H. Wang, Corros. Sci. 133, 165 (2018)
Y.H. Shu, F.H. Wang, W. Wu, Oxid. Met. 52, 463 (1999)
Y.H. Shu, F.H. Wang, W. Wu, Oxid. Met. 51, 97 (1999)
Y.H. Shu, F.H. Wang, W. Wu, Oxid. Met. 54, 5 (2000)
F.H. Wang, S. Geng, S. Zhu, Oxid. Met. 58, 185 (2002)
J.K. Kim, H.J. Park, D.N. Shim, Acta Metall. Sin. (Engl. Lett.) 29, 1107 (2017)
K.D. Ramkumar, R.J. Sai, G. Sridhar, V.S. Reddy, P. Prabaharan, N. Arivazhagan, N. Sivashanmugham, Acta Metall. Sin. (Engl. Lett.) 28, 196 (2015)
X.P. Zhuang, Y. Tan, X.G. You, P.T. Li, L.H. Zhao, C.Y. Cui, H.X. Zhang, H.Y. Cui, Vacuum 189, 110219 (2021)
H.J. Grabke, E. Reese, M. Spiegel, Corros. Sci. 37, 1023 (1995)
C. Wang, F. Jiang, F.H. Wang, Oxid. Met. 62, 1 (2004)
L. Liu, Y. Li, C.L. Zeng, F.H. Wang, Electrochim. Acta 51, 4736 (2006)
Y.B. Tang, L. Liu, Y. Li, F.H. Wang, J. Electrochemi. Soc. 158, C237 (2011)
L. Fan, L. Liu, M. Cao, Z.F. Yu, Y. Li, M.H. Chen, F.H. Wang, Metals 6, 72 (2016)
L. Fan, L. Liu, Z.F. Yu, M. Cao, Y. Li, F.H. Wang, Sci. Rep. 6, 29019 (2016)
Y.B. Tang, L. Liu, L. Fan, Y. Li, F.H. Wang, Materials 7, 6144 (2014)
R. Li, Y. Cui, L. Liu, R. Liu, L. Fan, M. Cao, Z.F. Yu, Z.Y. Chen, Q.J. Wang, F.H. Wang, J. Mater. Sci. Technol. 41, 595 (2021)
L.C. Chen, C. Zhang, Z.G. Yang, Corros. Sci. 53, 374 (2011)
C.H. Jiang, M. Feng, M.H. Chen, K. Chen, S.J. Geng, F.H. Wang, Corros. Sci. 187, 109484 (2021)
J. Peng, F. Moszner, J.L. Rechmann, D. Vogel, M. Palm, M. Rohwerder, Corros. Sci. 149, 123 (2019)
R. Swadźba, N. Laska, P.P. Bauer, Corros. Sci. 177, 108985 (2020)
G. Claudia, P. Alnegren, R. Faust, J. Svensson, J. Froitzheim, Int. J. Hydrog. Energy 43, 14665 (2018)
L. Fan, L. Liu, Y.H. Lv, H. Wang, A.Q. Fu, J.T. Yuan, Y. Li, F.H. Wang, C.X. Yin, Sci. Rep. 10, 16291 (2020)
T. Jonsson, B. Pujilaksono, H. Heidari, F. Liu, J.E. Svensson, M. Halvarsson, L.G. Johansson, Corros. Sci. 75, 326 (2013)
N. Israelsson, K. Hellström, J.E. Svensson, L.G. Johansson, Oxid. Met. 83, 1 (2014)
N. Israelsson, J. Engkvist, K. Hellström, M. Halvarsson, J.E. Svensson, L.G. Johansson, Oxid. Met. 83, 29 (2014)
N. Israelsson, K.A. Unocic, K. Hellström, T. Jonsson, M. Norell, J.E. Svensson, L.G. Johansson, Oxid. Met. 84, 269 (2015)
N. Israelsson, K.A. Unocic, K. Hellström, T. Jonsson, M. Norell, J.E. Svensson, L.G. Johansson, Oxid. Met. 84, 105 (2015)
S.C. Okoro, M. Kvisgaard, M. Montgomery, F.J. Frandsen, K. Pantleon, Surf. Eng. 33, 428 (2016)
G.S. Mahobia, N. Paulose, V. Singh, J. Mater. Eng. Perform. 22, 2418 (2013)
D. Pradhan, G.S. Mahobia, K. Chattopadhyay, V. Singh, Mater. Today 5, 7047 (2018)
T. Sanviemvongsak, D. Monceau, C. Desgranges, Corros. Sci. 170, 108684 (2020)
W.Y. Sun, J.L. Wang, L.L. Yang, M.H. Chen, Z.B. Bao, C.Y. Zheng, S.L. Zhu, F.H. Wang, Corros. Sci. 161, 108187 (2019)
C. Ciszak, I. Abdallah, I. Popa, J. Brossardc, A.V. Putb, D. Monceaub, S. Chevalier, Corros. Sci. 172, 108611 (2020)
E. Sadeghimeresht, L. Reddy, T. Hussain, Mater. Des. 148, 17 (2018)
Y. Shinata, Y. Nishi, Oxid. Met. 26, 201 (1986)
M. Juez-Lorenzo, V. Kolarik, W. Stamm, H. Fietzek, Mater. High Temp. 29, 229 (2014)
Y. Shinata, Oxid. Met. 27, 315 (1987)
N.N. Aung, Y.J. Tan, T. Liu, Corros. Sci. 48, 39 (2006)
R.J. Jiang, Y.W. Wang, X. Wen, C.F. Chen, J.M. Zhao, Appl. Surf. Sci. 412, 214 (2017)
J. Banaś, U. Lelek-Borkowska, B. Mazurkiewicz, W. Solarski, Electrochim. Acta 52, 5704 (2007)
C.H. Liang, H. Wang, N.B. Huang, J. Iron. Steel Res. Int. 21, 444 (2014)
C. Abreu, M. Cristóbal, R. Losada, X.R. Nóvoa, G. Pena, M.C. Pérez, Electrochim. Acta 51, 2991 (2006)
T. Jonsson, N. Folkeson, J.E. Svensson, L.-G. Johansson, M. Halvarsson, Corros. Sci. 53, 2233 (2011)
E. Liu, Z. Zheng, X. Guan, J. Tong, L.K. Ning, Y.S. Yu, J. Mater. Sci. Technol. 26, 895 (2010)
Acknowledgement
The work was financially supported by the National Natural Science Foundation of China (No. U22A20111).
Author information
Authors and Affiliations
Corresponding authors
Ethics declarations
Conflict of interest
The authors state that there are no conflicts of interest to disclose.
Additional information
Available online at http://springer.longhoe.net/journal/40195.
Rights and permissions
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Zhang, W., Cui, Y., Liu, L. et al. Corrosion Behavior of Pre-oxidized GH4169 Alloy with Solid NaCl Deposited in a Wet Oxygen Flow at 600 °C. Acta Metall. Sin. (Engl. Lett.) (2024). https://doi.org/10.1007/s40195-024-01699-9
Received:
Revised:
Accepted:
Published:
DOI: https://doi.org/10.1007/s40195-024-01699-9